Rubber like

code short description

mix ratio

[pbw]

potlife

[mins@40°C]

color

hardness

[shore_A]

tensile

strength

[MPa]

elongation

at break

[%]

tech

data

VC8200 Three-component system that allows to obtain elastomers with variable hardness from 35 to 95 Shore A. Strong at demoulding, excellent elongation, high tear strenght. see data sheet 2':00''/2':30'' straw/white 35 to 95 1.5 to 11.5 200 to 1300


VC8210 Soft system, hardness 40 Shore A. Strong at demoulding, excellent elongation and  tear strenght. 100:25 2':00''/3':00'' straw 40/45 4/6 350/450


VC8220 Medium hardness: 60 shore A. Strong at demoulding, excellent tear strength.

100:36

2':00''/3':00'' straw/white 60/65 6/8 250/350


VC8230

High hardness: 85 shore A. Strong at demoulding, excellent tear strength.

100:70 2':00''/3':00'' straw/white 85/90 17/19 150/250


Low modulus

code short description

mix ratio

[pbw]

potlife

[mins@40°C]

color

hardness

[shore_D]

flexural

modulus

[MPa]

Tg/Hdt*

[°C]

tech

data

VC8261 Polypropylene like, low flexural modulus, excellent impact resistance, high flexibility.  100:100

3':30''/4':30''

(@25°C)

straw 75/80 1100/1400 65/70


VC8261HT Polypropylene like, medium flexural modulus, high temperature resistance. 100:125

6':00''/9':00''

(@25°C)

amber 80/85 1700/2000 130*


High modulus

code short description

mix ratio

[pbw]

potlife

[mins@40°C]

color

hardness

[shore_D]

flexural

modulus

[MPa]

Tg/Hdt*

[°C]

tech

data

VC8250 Extremely rigid, strong at demoulding. Simulates thermoplastics such Nylon and Glass filled nylon.  100:120 3':00''/4':00'' straw 85/90 2900/3100 82/87


VC8262 High temperature ABS like, rigid, strong at demould, easily pigmentable. 100:100 2':00''/3':00''

yellow

brown

90 2500/2800 100


VC8264 White brilliant, low viscosity, quick demoulding. The components do not require preheating. Simulates PMMA and ABS. 100:100

7':00''/10':00''

(@25°C)

white 82/87 2300/2750 85/90


VC8265 Glass filled, Extremely rigid, strong at demould. Simulates glass filled nylon and other polyamides. 100:110 3':00''/4':00'' beige 87/92 2900/3300 90/95


High temperature

code short description

mix ratio

[pbw]

potlife

[mins@25°C]

color

hardness

[shore_D]

flexural

modulus

[MPa]

Tg/Hdt*

[°C]

tech

data

VC8292 ABS like, high temperature, impact and petrol resistance. Rapid demould, easily pigmentable. 100:150

6':00''/9':00''

amber 80/85 1800/2200 120*


VC8299

High thermal resistance, excellent mechanical properties and easily pigmentable. Simulates polycarbonate, PMMA and ABS.

 

100:130 5':30''/7':30'' amber 85/90 1950/2250 150/160*


Transparent

code short description

mix ratio

[pbw]

potlife

[mins@25°C]

color

hardness

[shore_D]

flexural

modulus

[MPa]

Tg/Hdt

[°C]

tech

data

VC8241 Optical transparency, UV stable, high heat distorsion temperature, high rigidity. Simulates polycarbonate, PMMA and ABS. Designed for casting up to 40mm. 100:150 7':00''/9':00'' colorless 85/90 2000 98

VC8298 Excellent mechanical properties and high optical transparency, UV stable. Simulates polycarbonate, PMMA and ABS. 100:140 6':30''/7':30'' colorless 85/90 1500/2000 130/140*


Flame retardant

code short description

mix ratio

[pbw]

potlife

[mins@25°C]

color

hardness

[shore_D]

flexural

modulus

[MPa]

Tg/Hdt*

[°C]

tech

data

VC3385 Excellent physical properties, low viscosity, high impact resistance and elasticity. Flame retardant (UL94 V-0). 100:120 7':00''/8':00'' straw 85/90 2250/2750

65/75*