mineral

  

code description application

dosage

[g/100g_resin]

apparent

density

[g/ml]

granulometry

[µm]

tech

data

F01 Alumina tri-hydrate, white powder, it reduces the heat of reaction and the shrinkage. Flame retardant agent. PU, UP, epoxy casting resins up to 200

1.35 ad

90/100 (d50)


F21 Alumina tri-hydrate, white powder, it reduces the heat of reaction and the shrinkage. Flame retardant agent. PU, UP, epoxy casting resins up to 200

0.90 ad

20/100 (d50)
F02 Calcium carbonate, white, easily workable, It reduces the shrinkage.  PU, UP, elastomers, adhesives 100 1.25 60


F18 Natural talc, light grey, with a lamellar structure. Used as a thixotropic and thickening agent. brushable products and putties 50 to 100 0.65 ad 20


F20 Natural barium sulphate, white, improves physical properties. putties, casting resins, coating 250 1.10 3 (d50)


F03 Staple cotton, white cotton fibers, used as a tixotropic and thickening agent. brushable products and putties 10 to 25 90

Ø=20

length=180


F04 Pyrogenic silica, white, low density, thixotropic filler. putties 1 to 5 50 200 m2/g(surface area) 


F29 Chopped strand glass, reinforcing agent used in structural bonding and grouting. fibrous putties 15 to 70 - length=3mm


F13 Ventilated quartz, white, high hardness and abrasiveness. flooring, casting resins 150 1.20 100


F14_26 Spherical quartz, grey, high hardness and compression resistant. flooring, moulds up to 1200 1.50

0.1 to 3.0mm


 metallic

code description application

dosage

[g/100g_resin]

apparent

density

[g/ml]

granulometry

[µm]

tech

data

F08 Atomized aluminium, grey, easy to work. It improves thermal conductivity. connecting layers, casting systems, adhesives up to 150 0.95 <100

F09 Aluminium granules. molds, casting systems 500 0.85/095 0.8-2.0mm


F17 Iron powder. molds, tools, casting systems 500 3.40 <100


 microspheres

code description application

dosage

[g/100g_resin]

apparent

density

[g/ml]

granulometry

[µm]

tech

data

F06 Hollow glass microspheres, grey, low density, moderate cost. It allow to obtain a final density less than 0,8 g/ml. Can be machined with hardened metal cutting tools. modelling paste, putties, casting systems 50 to 300 0.40 250

F05 Phenolic microspheres, reddish-brown, designed to reduce the weight of plastics, rubber, resins. Very easy to machine and sandable. syntactic pastes, adhesives, sealants 10 to 40 0.10 65


F26 Low density, white hollow microspheres, obtained from rhyolite. It improve tensile and impact resistance. Easily sandable. adhesives, putties, sealants 10 to 40 0.13/0.14 50 (d50)


F19 Expanded acrylic-copolymer white microspheres. It allow to obtain a final density less than 0,5 g/ml. coating, elastomers, adhesives,  1 to 3 0.02/0.04 35/55