Fast-cast

code short description color

mix ratio

[pbw]

geltime

[mins]

hardness

[shore_D]

flexural

modulus

[MPa]

Tg

[°C]

tech

data

PU8060 High mechanical strength and temperature resistance, fast demoulding. It allows to produce both prototypes and production series. beige 100:50 2 72 1100 102


PU8061 White, easily pigmentable, fast demoulding, recommended for models and prototypes. white 100:100 3 75 1420 81


PU8062 High hardness and flexural strength, good potlife. Recommended for reproductions of models and prototypes, pre-series. beige 100:100 4 75 1450 93


PU8065 Excellent mechanical properties, rigid, tough. pearl 100:100 9 84 2480 74


PU8070/1 Ultra-low viscosity, high definition, easy pigmentable, long potlife. Recommended for dental prototypes, positioning masks for trimming of thermoformed parts. ivory 100:100 5 73 1320 115


Mass-cast

code short description color

mix ratio

[pbw]

geltime

[mins]

hardness

[shore_D]

flexural

modulus

[MPa]

Tg

[°C]

tech

data

PU8092 Very long potlife, low exotherm, high mechanical properties. Recommended, when combined with mineral fillers, for mass casting applications. beige 100:70 45':00'' 78 2140 51


Aliphatic

code short description color

mix ratio

[pbw]

geltime

 

hardness

[shore_D]

flexural

modulus

[MPa]

Tg

[°C]

tech

data

PU8095

Two-component casting polyurethane, optically clear, UV stable, fast curing in thin thickness. Suitable for casting into RTV-2. Recommended thicknesses up to 10 mm.

 

colorless 100:110 12 mins 85 2300 64

PU8095-0.5

Two-component casting polyurethane, optically clear, UV stable, fast curing in thin thickness. Suitable for casting into RTV-2. Recommended thicknesses from 10 to 30 mm.

colorless   100:110 30 mins  85 2300  64 

PU8095-2

Two-component casting polyurethane, optically clear, UV stable, fast curing in thin thickness. Suitable for casting into RTV-2. Recommended thicknesses from 20 to 40 mm.

colorless  100:110  2 hours  85 2300  64 

PU8095-8

Two-component casting polyurethane, optically clear, UV stable, fast curing in thin thickness. Suitable for casting into RTV-2. Recommended mass casting.

colorless   100:110 8 hours  85 2300  64 

PU8097

Two-component transparent casting polyurethane,UV stable. Recommended for thicknesses from 5 to 30 mm. Not suitable for RTV-2 silicone moulds.

 

colorless

 

100:100 1 hour 80 2000 60


PU8098 Two-component transparent casting polyurethane,UV stable. Recommended for thicknesses from 20 to 60 mm. Not suitable for RTV-2 silicone moulds. colorless 100:100 4 hours 80 2000 60


PU8099 Two-component transparent casting polyurethane,UV stable. Recommended for thicknesses from 40 to 100 mm. Not suitable for RTV-2 silicone moulds.

colorless

100:100 24 hours 80 2000 60


Filled

code short description color

mix ratio

[pbw]

geltime

[mins]

hardness

[shore_D]

flexural

modulus

[MPa]

Tg

[°C]

tech

data

PU8130

PU 8130 is a two-component, filled, casting polyurethane system. Low shrinkage, easy workable, flame retardant.

grey  100:20  80  3370  87   
PU8160 Casting polyurethane, flame retardant, long potlife, UL94 V0. Designed for vacuum embedding of low and medium voltage measuring transformers up to 36kV.  brown 100:30  60  70  2680  52